BLR-896 is a rutile titanium dioxide pigment produced by the chloride process. It is specifically
designed for industrial coatings but also performs well in architectural coatings. With its optimized alumina and dense silica coating, it provides superior durability for the most demanding exterior applications, whilst also providing excellent optical and dispersion performance for superb visual appearance and formulation efficiency.
LOMON® R-996 is Zirconia and Alumina treated rutile titanium dioxide pigment. It has excellent outdoor durability and superior gloss.
Applications
LOMON® R-996 is recommended for exterior or interior use in high quality water-borne and solvent-borne architectural, industrial and powder coatings, inks and plastics industries.
TECHNICAL DATA SHEET
TYPE | R-996 |
Crystal Form | Rutile |
Classification ISO591 ，DIN55912 | R2 |
ASTM D476 | Ⅲ |
CAS No. | 13463-67-7 |
TiO2Content(%) min | 93.0 |
pH Value | 6.5~8.5 |
Density(g/cm3) | 4.0 |
Oil Absorption (g/100g) max | 22 |
Specific Resistance(Ω·m) min | 100 |
Average Particle Size(μm) | 0.23 |
Surface Treatment | Zirconia & Alumina; Organic |
COMPARABLE PRODUCT TEST REPORT
Alkyd Melamine Enamel Test:
| Binder | 32% coconut alkyd / butylated melamine=70/30 (solid) |
| Grinding | Red Devil 5400 Paint Conditioner |
| Enamel | Dry PVC 24% ，Pig / Binder solid=1.2 |
| Coating | For Gloss and Color evaluation ，coated with 150 micron wet thick applicator on a glassplate and baked for 20 minutes at 130 degree Centigrade. |
R-996 | Competitive A | Competitive B | Competitive C | |
Fineness of grinding | ( μm) | ( μm) | ( μm) | ( μm) |
For 3 min | 17 | 20 | 17 | 15 |
9 min | 14 | 17 | 13 | 12 |
15min | 12 | 16 | 12 | 10 |
21min | 10 | 15 | 10 | 8 |
40min | <5 | 12 | <5 | <5 |
60 Specular Gloss | 89 | 87 | 89 | 90 |
Color | ||||
L | 93.9 | 93.7 | 94.0 | 94.0 |
a | -1.0 | -0.9 | -0.9 | -1.0 |
b | 0.6 | 1.2 | 0.8 | 0.9 |
Whiteness | 93.8 | 93.5 | 93.9 | 93.8 |
Opacity | ||||
Y on black substrate | 75.6 | 74.7 | 75.8 | 75.7 |
Y on white substrate | 84.7 | 83.9 | 84.8 | 84.5 |
Contrast Ratio | 89.3 | 89.1 | 89.4 | 89.6 |
SAFETY & HEALTH INSTRUCTION
All Lomon TiO2 products including R996 are not hazardous article according to international standard. Material Safety Data Sheet will be provided.
PACKING & TRANSPORTION
25Kg, 500Kg and1000Kg, seaworthy and suitable for container transportation
Key Features
| High whiteness and opacity | Good weatherability |
| Excellent dispersion | High gloss |
Applications
Interior and exterior architectural coatings with requirements of high gloss and weatherability Water and solvent-based Industrial coatings
Automotive OEM coatings and refinishing coatings
High weatherability powder coatings
Coil coatings,building boardand marine protection coatings
Typical Properties:
| TiO2 content /% | ≥ 94.0 |
| Rutile crystal content | ≥98.5 |
| Inorganic coating | Alumina, Zirconia, Silica |
| Surface treatment | Al2O3, ZrO2 |
| Volatile constituents at 105℃ | ≤ 0.5 |
| Residue, 45μm /% | ≤ 0.01 |
| pH | 6.0-9.0 |
| Resistivity, Ω·m | ≥ 80 |
| Oil absorption, g/100g | ≤ 18 |
| CIE L* | ≥ 98.0 |
| CIE b* | ≤ 1.0 |
| Specific gravity, g/cm3 | 4.1 |
Classifications:
ASTM D476 - 00 (2000) Type VII
EINECS number 236-675-5
Color Index 77891, Pigment White 6
ISO 591- 1:2000 Type R2
CAS number 13463-67-7
Safety
Good industrial hygiene practice should be used to avoid the generation of dust. Please refer to the Material Safety Data Sheet for more information on the handling of this product.
Storage
This product should not be stored outside or exposed to weather. All direct contact with moisture should be avoided.
Packaging
Titanium dioxide pigments are available in 25kg compound paper bag, 500kg and 1000kg plastic woven bag.
Contact With Us:
E-mail: wangxingqiang@ericwchem.com
Have a Questions? Call Us:
Add:
Building A1, Jiete Industrial Park, Huangpu District, Guangzhou City, Guangdong Province, China
English
Español
русский
tiếng việt